+86-371-64599000

sale@literefractory.com

Material refractario Henan Lite Co.Ltd.

Stone Broken Machine Manufacturers China

Hot Products
  • Ladrillos AZS

    Ladrillos AZS AZS arch crown refractory block/brick is manufactured using high quality zirconia and zirconium corundum clinker raw materials with ceramic and chemical bonding.It is shipped underhigh pressure and fired with high temperature with scientifi

  • ladrillo con alto contenido de

    ladrillo con alto contenido de El ladrillo con alto contenido de almina es un tipo de refractario, la composicin principal de este ladrillo refractario es Al2O3. El trixido de aluminio (Al2O3) que contiene ms del 48% de refractarios de silicato de aluminio. ►Detalles:

  • Ladrillo aislante de mullita

    Ladrillo aislante de mullita El ladrillo aislante ligero de mullita se fabrica con mullita pura y polvo de almina aadido segn el tipo de sinterizacin a alta temperatura. ►Caractersticas: 1. Bajos niveles de hierro y otras impurezas . 2. Alta resistencia mecnica . 3.

  • cemento refractario

    cemento refractario ►Descripcin: El cemento refractario tambin se conoce como cemento de bauxita, cemento de alta almina o cemento de aluminato. 1. Cemento refractario general: fabricado con bauxita de alta almina y piedra caliza . 2. Cemento refractario de

  • Fundible con alto contenido de

    Fundible con alto contenido de Fabricado con agregados con alto contenido de almina, polvo refractario, aglutinantes y otros aditivos. ► Presenta alta resistencia mecnica, buena resistencia al choque trmico y a la abrasin. Se utiliza principalmente como revestimiento d

Magnesia-alumina spinel bricks



►Raw material:
High purity magnesia or fused magnesia,fused spinel
 
►Feature:
1.High thermal shock resistance stability,
2.Good corrosion resistance,
3.High mechanical strength at high temperature,
4. Good resistance to abrasion,
5.Good kiln coating adherence,
6. Chromium-free and pro-environment.



►Technical data
Item Quality 1 Quality 2
MgO ≥86% ≥86%
Al2O3 10%-12% 5%-8%
Bulk density ≥2.98g/cm3 ≥2.98g/cm3
Apparent porosity  ≤15% ≤15%
Cold crushing strength ≥80Mpa ≥80Mpa
Refractoriness under load ≥1700°C ≥1700°C
1100°C, water-cooling Thermal shock resistance ≥10cycle ≥10cycle
Use part  Transitional zone High temperature areas
 
►Application:
special used for cement rotary kiln.

►Delivery
Package Informations:
1. Packed in a 100cm*100cm fumigated wooden pallet with a waterproof plastic film cover, and tightened with plastic bandages.
2. We can also pack the goods according to your requirements.

Shipping:
1. FEDEX/DHL/UPS/TNT for samples.
2. By Sea for batch goods.
3. Customers specifying freight forwarders or negotiable shipping methods!
4. Delivery Time:3 days for common shape samples;15 days for special shape samples.Within 30 days for batch goods.


Copyright © Henan Lite Refractory Material Co.Ltd. Todos los derechos reservados.

   
#
Contáctenos
¡Obtenga la lista de precios más actualizada aquí!
Enviar mensajes

Si necesita más detalles sobre nuestros productos, escriba lo que necesita, nos comunicaremos con usted lo antes posible con precios favorables.!