+86-371-64599000

sale@literefractory.com

Material refractario Henan Lite Co.Ltd.

Stone Broken Machine Manufacturers China

Hot Products
  • Ladrillos AZS

    Ladrillos AZS AZS arch crown refractory block/brick is manufactured using high quality zirconia and zirconium corundum clinker raw materials with ceramic and chemical bonding.It is shipped underhigh pressure and fired with high temperature with scientifi

  • ladrillo con alto contenido de

    ladrillo con alto contenido de El ladrillo con alto contenido de almina es un tipo de refractario, la composicin principal de este ladrillo refractario es Al2O3. El trixido de aluminio (Al2O3) que contiene ms del 48% de refractarios de silicato de aluminio. ►Detalles:

  • Ladrillo aislante de mullita

    Ladrillo aislante de mullita El ladrillo aislante ligero de mullita se fabrica con mullita pura y polvo de almina aadido segn el tipo de sinterizacin a alta temperatura. ►Caractersticas: 1. Bajos niveles de hierro y otras impurezas . 2. Alta resistencia mecnica . 3.

  • cemento refractario

    cemento refractario ►Descripcin: El cemento refractario tambin se conoce como cemento de bauxita, cemento de alta almina o cemento de aluminato. 1. Cemento refractario general: fabricado con bauxita de alta almina y piedra caliza . 2. Cemento refractario de

  • Fundible con alto contenido de

    Fundible con alto contenido de Fabricado con agregados con alto contenido de almina, polvo refractario, aglutinantes y otros aditivos. ► Presenta alta resistencia mecnica, buena resistencia al choque trmico y a la abrasin. Se utiliza principalmente como revestimiento d

Precautions for application of refractory cement

When refractory cement is used for baking in industrial kilns, the following matters must be paid attention to:
1.At the normal temperature stage of 350°C, local bursting is most likely to occur, so special attention should be paid to slow baking. If a large amount of steam still emerges after insulation at 350℃, the heating rate should still be slowed down.
2.Under conditions where ventilation is poor and water vapor cannot be easily discharged, the heat preservation time should be appropriately extended.
3.When baking with heavy oil, be careful not to spray heavy oil on the surface of the furnace lining to prevent local bursting.
4.When baking with firewood, direct contact with the flame often causes excessive local heating and should be protected.
5.For newly poured refractory cement, it must be baked for at least 3 hours.
6.The cooling of the refractory cement furnace lining should also be slow and forced ventilation should be avoided.

Copyright © Henan Lite Refractory Material Co.Ltd. Todos los derechos reservados.

   
#
Contáctenos
¡Obtenga la lista de precios más actualizada aquí!
Enviar mensajes

Si necesita más detalles sobre nuestros productos, escriba lo que necesita, nos comunicaremos con usted lo antes posible con precios favorables.!